A new material designed for photovoltaic applications
In developed countries, the advantages of integrated photovoltaic systems for buildings are increasing. In the context of increasing global energy costs, in order to assess the potential of photovoltaic building integration, architects and engineers are studying the use of photovoltaics for glass curtain walls and roofs and cost-effective integrated solutions, because photovoltaic modules themselves are a A special kind of laminated glass (encapsulated solar crystalline silicon wafer), then by producing photovoltaic modules with new safety and protection characteristics, it will have its own advantages. This new development makes photovoltaic building integration more attractive to architects and adds new opportunities to the future of photovoltaic module manufacturers, the construction industry, and the glass industry.
Huakai, as one of the largest PVB interlayer suppliers in China in the construction and automotive industry, developed it for its deep understanding of the growing importance of the photovoltaic market in the field of renewable energy. Used in special photovoltaic PVB interlayer. The solar cell module of the PVB interlayer for photovoltaic modules produced by Huakai shows high transparency, high adsorption power and excellent thermal insulation, ultraviolet protection, and moisture resistance. They are still highly reliable when exposed to harsh outdoor weather conditions for long periods of time.
After Huakai PVB interlayer film is laminated and cross-linked and cured, it can not only increase the bonding degree of the battery module, enhance the efficiency of the solar cell module, but also provide mechanical, thermal and optical protection for the module, extend the service life of the module, and increase the cost. benefit.
Technical parameters of photovoltaic grade PVB
Feature |
unit |
Tech-standards |
Detection method |
Density |
g/cm3 |
1.070 |
GB/T1033-1986 |
Tensile strength |
Mpa |
≥22 |
GB/T1040-1992 |
Elongation at break |
% |
>200 |
GB/T1040-1992 |
Moisture content |
% |
0.35-0.55 |
企标 |
Transmittance |
% |
≥89 |
GB/T2410-1998 |
Haze |
% |
≤0.4 |
GB/T2410-1998 |
Thermal expansion |
℃-1 |
2.2×10-4 |
GB/T1036-1989 |
Volume resistivity |
ΩCm×1011 |
8.0 |
GB/T1014-2006 |
Adhesive strength |
N/cm |
≥20 |
GB/T1751-1998 |
Yellowing index |
N/A-- |
≤12 |
HG/T3862-2006 |
UV shielding |
300-400nm |
≤4.0 |
-- |
Photovoltaic grade transparent sheet (0.50/0.76mm)
Thickness |
0.50/0.76mm |
|
colour |
Transparent film |
Porcelain white |
Width |
650-2440 |
|
Length |
300/200 |